Our Advantage:
1. Cost price controlled well, lower price.
2. High precision.
3. Good quality, material: GE/HSQ, high purity, silica > 99.99% , high purity, silica > 99.99%.
4. High temperature-resistant, good corrosion-resistant and light transmittance.
5. Sample available.
6. Accept reworking if quality is not reach your requirements.
Description: 1. | Our clear fused quartz glass boats are produced with the advantaged continuous melting method and controlled by automatic control system. | 2. | These products are high purity, good spectral transmission, well controlled dimension and low OH, etc. | 3. | We can produce very large diameter rang boats. | 4. | We also can apply some further processing like trim cutting, fire polishing, bending, pinching, grinding and others according to customer´s requirements. | 5. | The OH content can be controled within 20ppm 15ppm10ppm5ppm2ppm as your special needs. |
|
Application:
Chemical Industries, Electric Light Source, Laboratories,Medical equipment, metallurgy , Optical,Photovoltaic,Photo communications,Research,Schools,Semiconductor,Solar,etc
Physical Properties:
1. Purity | SiO2 content is more than 99.99% |
2. Temperature | Softening point temperature is about 1730 degrees Celsius ,1100 degrees Celsius in a long time used ,short-time maximum use temperature is up to 1450 degrees Celsius |
3. Anti-corrosion | Quartz glass is acidic materials, except hydrofluoric acid and 300 degrees Celsius thermal phosphoric acid, on any other acids were shown to be inert, is the best anti acid materials. At room temperature, alkali and salt on quartz glass corrosion degree is minimal |
4. Transmittance good performance | Compare to ordinary silicate glass, transparent quartz glass in the whole wavelength head excellent permeability. In the infrared spectrum through than ordinary glass; in the visible region, quartz glass transmittance is relatively high ,above 85%-90%. In the UV spectral region especially in the ultraviolet region, the spectral transmission is much better than other glass,about 80% |
5. Good electrical insulation properties | Quartz glass with high dielectric strength and very low electrical conductivity, even in high temperature, high pressure and high frequency,it can still maintain high dielectric strength and resistance, in the application of the band almost no dielectric loss, therefore the quartz glass is an excellent high temperature dielectric insulating material |
6.Thermal stability | The thermal expansion coefficient of quartz galss is extremely small ,it can be able to adapt drastic temperature changes |
Precision
Range of OD | OD | WT | Siding | Out of Round | Bow/1000mm |
10mm Max | ±2.00% | ±10% | 12% | 2.0% | 2.0mm |
10 - 20mm | ±1.25% | ±8% | 10% | 1.5% | 2.0mm |
20 - 30mm | ±1.00% | ±10% | 15% | 1.5% | 2.0mm |
30 - 50mm | ±1.00% | ±10% | 15% | 1.5% | 2.0mm |
50 - 100mm | ±1.00% | ±12% | 15% | 2.0% | 2.0mm |
100 - 200mm | ±1.00% | ±12% | 15% | 2.0% | 2.0mm |
Corrosion Amaunt
H2SO4 | Density 1.84,2h,20°C,g/cm2 | 1.4*10-8 |
HNO3 | Density 1.4,2h,20°C,g/cm2 | 5*10-8 |
HCL | Density 1.19,2h,20°C,g/cm2 | 15*10-8 |
NaOH | 1%,2h,110°C,g/cm2 | 166*10-6 |
KOH | 1%,2h,98°C,g/cm2 | 68*10-6 |
Thermal Properties
CoefficientofExpansion(20°C~350°C) | 5.5*10-7/°C |
Thermal Conductivity(W/m°C,20°C) | 1.4 |
Specific Heat(J/kg,20°C) | 670 |
Softening Point( viscosity) | 1730°C |
Annealing Point | 1215°C |
Deformation Temperature(long time heat retaining) | 1120°C |
Mechanical Properties
Density g/cm3 | 2.2 |
Compression Strength N/mm2 | 1100 |
Bending Strength N/mm2 | 67 |
Tension Strength N/mm2 | 48 |
Micro Hardness N/mm2 | 8600~9800 |
Moh's hardnessMoh's hardness | 5.5~6.5 |
Electrical Properties
Electrical Resistivity(350°C,omh-cm) | 7*107 |
Insulating Strength(20°C,KV/cm) | 250~400 |
Dielectric Constant | 3.7 |